WHAT IS SAND CASTING?
Sand casting is a versatile manufacturing process used to create metal parts by pouring molten metal into a sand mould.
The process begins with the creation of a pattern, representing the final shape and dimensions of the part, which is then placed in a two-part sand mould. Once the mould is prepared, the pattern is removed, leaving behind a precise impression of the desired part. Molten metal is poured into the mould cavity, where it solidifies and takes on the shape of the part. After cooling, the sand mould is broken apart to reveal the metal casting inside.
At A & M Manufacturing Company Ltd. Our associated sand casting foundries are capable of producing a wide range of metal parts, from small components to large machinery parts, and can be used with both ferrous and non-ferrous metals. Examples of parts produced using this technique include engine blocks, cylinder heads, gears, pulleys, and ornamental metalwork.
SAND CASTING PROCESS
1. Pattern Making
The first step is creating a pattern that represents the shape of the desired casting. Patterns are typically made from materials like wood, metal, or plastic and are designed to be slightly oversized to compensate for metal shrinkage during cooling. The pattern includes allowances for machining and draft, facilitating its removal from the mould.
2. Mould Making
The mould is made by packing special moulding sand around the pattern in a moulding box, known as a flask. The moulding sand is mixed with clay and water or other bonding agents to help it retain its shape. The process involves two halves of the mould: the cope (top half) and the drag (bottom half). The pattern is placed in the drag, and sand is packed around it. Then, the cope is placed on top, and sand is packed into it as well. Once the sand has been compacted, the pattern is carefully removed, leaving a cavity that mirrors the shape of the pattern.
3. Core Making
If the casting requires internal cavities or undercuts, cores made of sand are used. These cores are formed in separate core boxes and are positioned in the mould cavity before the molten metal is poured. They remain in place during casting to form the internal features of the part.
4. Melting and Pouring
The metal, which can vary from iron, steel, aluminium, bronze, and more, is melted in a furnace to a specific temperature. Once the metal reaches the desired temperature and is thoroughly molten, it`s carefully poured into the mould cavity. Pouring must be done at a controlled rate to avoid turbulence and splashing, which can create defects in the casting.
5. Cooling
After the molten metal has been poured, it begins to cool and solidify within the mould. The cooling time can vary based on the metal used and the size of the casting. It`s crucial to allow the metal to cool completely to ensure the integrity and strength of the casting.
6. Mould Breakaway
Once the metal has solidified, the sand mould is broken apart to release the casting. This step is irreversible; moulds made from sand are destroyed during the casting removal, meaning a new mould is needed for each casting.
7. Cleaning and Finishing
The casting is then cleaned of any sand, scale, and excess metal from the gates, runners, and risers used to channel the molten metal into the mould. Cleaning can involve processes like shot blasting, grinding, and cutting. Further finishing processes, such as machining, painting, or coating, may be applied to achieve the desired surface finish and dimensional accuracy.
8. Inspection
Finally, the casting undergoes various inspections for quality assurance, including dimensional accuracy, surface finish, and structural integrity. Non-destructive testing methods such as X-ray, ultrasonic, or magnetic particle inspection may be used to detect internal defects.
What is the electric three-ball valve
Electric three-piece threaded ball valve small size, electric three-piece ball valve is composed of three parts of the valve housing, the four longer bolts from both ends of the middle of the valve body and valve ball made. The advantage is that without removing the pipe thread for disassembly and dismantling, the four bolts can be removed directly, and the middle part of the valve body can be removed. The working principle is also through the 90-degree rotation of the pneumatic actuator to drive the rotation of the ball in order to achieve the circulation and blocking media. The direct connection of the actuator to the valve body reduces the chances of failure. Suitable for light industrial machinery small space and narrow space occasions.